- Mechanical Properties
Value Units Test Method / Conditions Charpy Notched Impact Strength (cond) 5 kJ/m2 ISO 179-1/1eA Hardness (Cond) 82 Shore D ISO 868 Charpy Notched Impact Strength (dam) 3 kJ/m2 ISO 179-1/1eA Hardness (Dam) 87 Shore D ISO 868 Charpy Unnotched Impact Strength (cond) 60 kJ/m2 ISO 179-1/1eU Charpy Unnotched Impact Strength (dam) 40 kJ/m2 ISO 179-1/1eU Elongation at Break (cond) 11 % ISO 527-2/1A Elongation at Break (dam) 7 % ISO 527-2/1A Flexural Modulus (cond) 1800 MPa ISO 178 Flexural Modulus (dam) 3800 MPa ISO 178 Izod Notched Impact Strength (cond) 7 kJ/m2 ISO 180/1A Izod Notched Impact Strength (dam) 3.5 kJ/m2 ISO 180/1A Stress at Break (cond) 60 MPa ISO 527-2/1A Stress at Break (dam) 80 MPa ISO 527-2/1A - Thermal Properties
Value Units Test Method / Conditions Heat Deflection Temperature 95 °C ISO 75-2/Af Melting Point 260 °C ISO 11357-3 - Electrical Properties
Value Units Test Method / Conditions CTI (A2 Z G30) 450 V CEI 60112 - Physico-Chemical Properties
Value Units Test Method / Conditions Density 1.35 g/cm3 ISO 1183-1 Water Absorption (at 24H / 23°C) 0.75 % ISO 62 Water Absorption (at 30Min / 100°C) 1.1 % ISO 62
Technical Details & Test Data
- Note
- The values indicated above have been realized with standard specimens in room temperature, except if particular conditions:
- dam: specimens 48h after molding
- cond: specimens conditioned according to ISO 291 et ISO 1110. These datas must be considered as indicative values, but in no case as minimum values. Moreover, the design of the mold/die, the processing conditions and the color may have an impact on the properties. The information given herein is the outcome of our research and experience. It is given in all good faith but can neither be interpreted as a warranty given by us nor incur our liability especially in the event of infringement of third party rights.