Properties
- Mechanical Properties
Value Units Test Method / Conditions Tensile Strength 20 MPa ISO 527 Charpy Notched Impact Strength (at 23°C) 6 kJ/m2 ISO 179-1/1eA Hardness 70 Shore D ISO 868 Hardness 70 Shore D ISO 7619-1 Charpy Unnotched Impact Strength (at 23°C) 80 kJ/m2 ISO 179-1/1eU Yield stress 25 MPa ISO 527 Strain at break 50 % ISO 527 Elongation at Break 50 % ISO 527-2/1A Flexural modulus, 23° 2300 MPa ISO 178 Flexural Modulus 2300 MPa ISO 178 Izod Notched Impact Strength 6 kJ/m2 ISO 180/1A Charpy notched impact strength (+23°) 6 kJ/m2 ISO 179/1eA Charpy impact strength (+23°) N kJ/m2 ISO 179/1eU Stress at Break 20 MPa ISO 527-2/1A Stress at Yield Point 25 MPa ISO 527-2/1A - Physical Properties
Value Units Test Method / Conditions Melt Volume Flow Rate - MVR (230°C/2.16 kg) 6 cm3/10 min ISO 1133 Density 1040 kg/m3 ISO 1183 - Thermal Properties
Value Units Test Method / Conditions Temperature of deflection under load (1.80 Mpa) 65 °C ISO 75-1/-2 Melting temperature (10°C/min) 167 °C ISO 11357-1/-3 Heat Deflection Temperature 65 °C ISO 75-2/Af Melting Point 165/168 °C ISO 11357-3 Vicat Softening Point 152 °C ISO 306/A50 Vicat softening temperature 152 °C ISO 306 - Electrical Properties
Value Units Test Method / Conditions CTI min. 600 V CEI 60112 - Physico-Chemical Properties
Value Units Test Method / Conditions Density 1.04 g/cm3 ISO 1183-1 MVI (at 230°C-2.16Kg) 6 cm3/10min ISO 1133-1 - Fire Resistance
Value Units Test Method / Conditions Falling Ball Test 132 °C CEI 60695-10-2
Technical Details & Test Data
- Note
- The LOI measures are obtained through standard specimens of type I, with ignition of type A.
- The values indicated above have been realized with standard specimens which are conditionned according to ISO 291. These datas must be considered as indicative values, but in no case as minimum values. Moreover, the design of the mold/die, the processing conditions and the color may have an impact on the properties.