Enhanced TDS
Knowde-enriched technical product data sheet
Identification & Functionality
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
Properties
- Mechanical Properties
Value Units Test Method / Conditions Charpy Notched Impact Strength (at 23°C) 6 kJ/m2 ISO 179-1/1eA Hardness 68 Shore D ISO 868 Charpy Unnotched Impact Strength (at 23°C) 57 kJ/m2 ISO 179-1/1eU Elongation at Break 20 % ISO 527-2/1A Flexural Modulus 2100 MPa ISO 178 Izod Notched Impact Strength 5.5 kJ/m2 ISO 180/1A Stress at Break 20 MPa ISO 527-2/1A Stress at Yield Point 23 MPa ISO 527-2/1A - Thermal Properties
Value Units Test Method / Conditions Heat Deflection Temperature 59 °C ISO 75-2/Af Melting Point 165/168 °C ISO 11357-3 Vicat Softening Point 146 °C ISO 306/A50 - Electrical Properties
Value Units Test Method / Conditions CTI min. 600 V CEI 60112 - Physico-Chemical Properties
Value Units Test Method / Conditions Density 1.04 g/cm3 ISO 1183-1 MVI (at 230°C-2.16Kg) 20 cm3/10min ISO 1133-1 - Fire Resistance
Value Units Test Method / Conditions Falling Ball Test 127 °C CEI 60695-10-2 Incandescent Glow Wire Flammability Test (at 2mm) 750 / 5 °C /s CEI 60695-2-12
Technical Details & Test Data
- Note
- The LOI measures are obtained through standard specimens of type I, with ignition of type A.
- The values indicated above have been realized with standard specimens which are conditionned according to ISO 291. These datas must be considered as indicative values, but in no case as minimum values. Moreover, the design of the mold/die, the processing conditions and the color may have an impact on the properties.