ACP Composites 8.8 oz Fiberglass 8-Harness Satin Weave RTS Prepreg

ACP Composites 8.8 oz Fiberglass 8-Harness Satin Weave RTS Prepreg is a Satin Weave EGlass fabric impregnated with a thermosetting epoxy resin system. . It is storable at room temperatures and does not require freezer storage. With the long out life of the resin matrix, the carbon fiber prepreg can be shipped and handled at room temperatures. It is ideal for use when a long shelf life is desired, high-temperature capabilities are not required and controlled resin content is wanted.

Polymer Name: Epoxy Resins & Compounds

Functions: Prepreg

Reinforcement Material: Glass Fibers

Technical Data Sheet

Enhanced TDS

Knowde-enriched technical product data sheet

Identification & Functionality

Chemical Family
Epoxy & Epoxy Derivatives
Polymer Name
Epoxy Resins & Compounds
Reinforcement Form
Satin Weave Fabric
Reinforcement Material
Glass Fibers
Composite Materials Functions
Prepreg
Resin Type
Thermosetting Epoxy
Technologies
Composite Materials
Product Families
Composite Materials — Prepregs & Molding Compounds
Thermoset Prepregs

Features & Benefits

Materials Features
Long Shelf Life

Applications & Uses

Markets
Automotive & Transportation,
Consumer Goods
Applications
Automotive & Transportation — Automotive
Exterior & Body,
Interior
Consumer Goods — Sports & Recreation
Automotive & Transportation — Transportation
Aerospace & Aviation
Cure Cycles

There are three optional cure cycles. All three will produce similar properties.

  • 5°F-per-minute ramp up to 310°F (154°C)
  • Hold for 1 hour
  • <5°F-per-minute ramp down to at least 150°F (66°C) before removing from oven
  • 5°F-per-minute ramp up to 290°F (154°C)
  • Hold for 2 hours
  • <5°F-per-minute ramp down to at least 150°F (66°C) before removing from oven.
  • 5°F-per-minute ramp up to 270°F (154°C)
  • Hold for 4 hours
  • <5°F-per-minute ramp down to at least 150°F (66°C) before removing from oven

Properties

Physical Form
Fabric
Fiber Type
E-Glass
Typical Properties
ValueUnitsTest Method / Conditions
Resin Content30% by Weight-
Density1.229g/cc-
Tg (fromG" DMA curve)270°F-
Tensile Strength10.7ksi-
Tensile Modulus440ksi-
Elongation at Break4%-
Tg after 24hr Water Boil169°F-
Operation Temp. (below the resin Tg)60-70°F-

Packaging & Availability

Availability
  • Weight = 8.81 oz/yd^2
  • Thickness = .008"

Storage & Handling

Shelf Life and Storage

The material should remain sealed when not is use and be stored indoors, out of the weather.

  • The shelf life is 6 months from the date of manufacture when the maximum storage temperature shall not exceed 90°F (32°C).
  • The shelf life is 12 months from the date of manufacture when the maximum storage temperature shall not exceed 75°F (24°C).
  • The shelf life is 30 months from the date of manufacture when the maximum storage temperature shall not exceed 0°F (-18°C), with an additional 6 months at <75 °F (24°C).