Addilene® PMD 50384

Identification & Functionality

Additives Included

Impact Modifier

Chemical Family

Polyolefins,

Polypropylenes (PP)

Polymer Name

Polypropylene Copolymer

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Basic Thermoplastics

Polyolefins

Features & Benefits

Materials Features

Good Scratch Resistance,

Good Thermal Stability,

Heat Resistance,

Impact Modified,

Light Weight,

Low Emissions,

Low Odor

Applications & Uses

Markets

Automotive & Transportation

Applications

Automotive & Transportation — Automotive

Exterior & Body,

Interior

Automotive & Transportation — Other Automotive & Transportation Applications

Plastics & Elastomers End Uses

Automotive Applications,

Automotive Exterior Parts,

Automotive Instrument Panel,

Automotive Interior Parts,

Consoles,

Door Panel,

Instrument Panel

Properties

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Strength	17	MPa	ISO 527
Charpy Notched Impact Strength (at 23°C)	18	kJ/m2	ISO 179-1/1eA
Strain at Break	min. 50	%	ISO 527
Hardness	65	Shore D	ISO 868
Hardness	65	Shore D	ASTM D 2240
Charpy Unnotched Impact Strength (at 23°C)	NB	kJ/m2	ISO 179-1/1eU
Yield stress	21	MPa	ISO 527
Elongation at Break	min. 50	%	ISO 527-2/1A
Flexural modulus, 23°	1050	MPa	ISO 178
Flexural Modulus	1000	MPa	ISO 178
Izod Notched Impact Strength	NB	kJ/m2	ISO 180/1A
Charpy impact strength (+23°)	N	kJ/m2	ISO 179/1eU
Charpy notched impact strength (+23°)	17	kJ/m2	ISO 179/1eA
Stress at Break	15	MPa	ISO 527-2/1A
Stress at Yield Point	20	MPa	ISO 527-2/1A

Physical Properties

	Value	Units	Test Method / Conditions
Melt Volume Flow Rate - MVR (230°C/2.16 kg)	16	cm3/10 min	ISO 1133
Density	900	kg/m3	ASTM D 792

Thermal Properties

	Value	Units	Test Method / Conditions
Temperature of deflection under load (1.80 Mpa)	52	°C	ISO 75-1/-2
Melting temperature (10°C/min)	167	°C	ISO 11357-1/-3
Heat Deflection Temperature	55	°C	ISO 75-2/Af
Melting Point	165/168	°C	ISO 11357-3
Vicat Softening Point	140	°C	ISO 306/A50
Vicat softening temperature	143	°C	ISO 306

Typical Properties

	Value	Units	Test Method / Conditions
Shrinkage	1.6	%	interne
Shrinkage	1.7	%	interne

Electrical Properties

	Value	Units	Test Method / Conditions
CTI	min. 600	V	CEI 60112

Physico-Chemical Properties

	Value	Units	Test Method / Conditions
Density	0.9	g/cm3	ISO 1183-1
MVI (at 230°C-2.16Kg)	15	cm3/10min	ISO 1133-1

Fire Resistance

	Value	Units	Test Method / Conditions
Falling Ball Test	120	°C	CEI 60695-10-2