Properties
- Mechanical Properties
- Thermal Properties
- Typical Properties
Value | Units | Test Method / Conditions | |
Tensile Modulus (Dry) | 17500 | Mpa | ISO 527-1 527-2 |
Charpy Impact Strength (Conditioned to Equilibirium at 23°C, 50%RH) | 40 | kg/m² | ISO 179-1 |
Charpy Impact Strength (Dry-as-Mold Condition) | 35 | kg/m² | ISO 179-1 |
Tensile Modulus (Condition) | 13000 | Mpa | ISO 527-1 527-2 |
Charpy Impact Strength (Conditioned) | 40 | kg/m² | ISO 179-1 |
Tensile Strain at Break (Dry) | 1.3 | % | ISO 527-1 527-2 |
Charpy Notched Impact Strength (Dry-as-Mold Condition) | 5 | kg/m² | ISO 179-1 |
Tensile Strain at Break (Condition) | 1.7 | - | - |
Charpy Impact Strength (Dry) | 35 | kg/m² | ISO 179-1 |
Charpy Notched Impact Strength (Conditioned to Equilibirium at 23°C, 50%RH) | 6 | kg/m² | ISO 179-1 |
Charpy Notched Impact Strength (Conditioned) | 6 | kg/m² | ISO 179-1 |
Charpy Notched Impact Strength (Dry) | 5 | kg/m² | ISO 179-1 |
Flexural Modulus (Conditioned to Equilibirium at 23°C, 50%RH) | 12000 | Mpa | ISO 178 |
Flexural Modulus (Conditioned) | 12000 | Mpa | ISO 178 |
Flexural Modulus (Dry-as-Mold Condition) | 15000 | Mpa | ISO 178 |
Flexural Modulus (Dry) | 15000 | Mpa | ISO 178 |
Flexural Strength (Dry-as-Mold Condition) | 240 | Mpa | ISO 178 |
Flexural Strength (Conditioned to Equilibirium at 23°C, 50%RH) | 200 | Mpa | ISO 178 |
Flexural Strength (Conditioned) | 200 | Mpa | ISO 178 |
Flexural Strength (Dry) | 240 | Mpa | ISO 178 |
Tensile Modulus (Dry-as-Mold Condition) | 17500 | Mpa | ISO 527-1 527-2 |
Tensile Modulus (Conditioned to Equilibirium at 23°C, 50%RH) | 13000 | Mpa | ISO 527-1 527-2 |
Tensile Strain at Break (Dry-as-Mold Condition) | 1.3 | % | ISO 527-1 527-2 |
Tensile Stress at Break (Dry-as-Mold Condition) | 164 | Mpa | ISO 527-1 527-2 |
Tensile Strain at Break (Conditioned to Equilibirium at 23°C, 50%RH) | 1.7 | % | ISO 527-1 527-2 |
Tensile Strain at Break (Conditioned) | 1.7 | % | ISO 527-1 527-2 |
Tensile Stress at Break (Conditioned to Equilibirium at 23°C, 50%RH) | 129 | Mpa | ISO 527-1 527-2 |
Tensile Stress at Break (Conditioned) | 129 | Mpa | ISO 527-1 527-2 |
Tensile Stress at Break (Dry) | 164 | Mpa | ISO 527-1 527-2 |
Value | Units | Test Method / Conditions | |
Coefficient of Linear Thermal Expansion (Dry-as-Mold Condition) | 1.5 | 10⁻⁵/°C | ISO 11359-2 |
Deflection Temperature (Under load 0.45MPa) | 194 | °C | ISO 75-2 |
Deflection Temperature (Under load 1.8MPa) | 91 | °C | ISO 75-1 |
Coefficient of Linear Thermal Expansion | 1.5 | 10⁻⁵/°C | ISO 11359-2 |
Coefficient of Linear Thermal Expansion (Conditioned to Equilibirium at 23°C, 50%RH) | 1.5 | 10⁻⁵/°C | ISO 11359-2 |
Value | Units | Test Method / Conditions | |
Mold Shrinkage (Thickness : 3.2mm, Flow) | 0.1 | % | - |
Mold Shrinkage (Thickness : 3.2mm, Transverse) | 0.5 | % | - |
Water Absorption (23°C, 50% RH Equilibirium) | 1 | % | ISO 62 |
Density | 1.66 | g/cm³ | ISO 1183 |