LNP LUBRICOMP™ Compound - 2X00858 - SABIC's Specialty

Identification & Functionality

Additives Included: Mold Release Agent
Chemical Family: Fluoropolymers,
Polyolefins
Fillers Included: Glass Fiber,
PTFE,
Proprietary
Polymer Name: Perfluoroethylene Propylene Copolymer (FEP)
Plastics & Elastomers Functions: Resin
Technologies: Plastics
Product Families: Plastics — Engineering & Specialty Polymers
High Performance Thermoplastics

Features & Benefits

Materials Features: Dimensional Stability,
Friction Resistant,
Good Mold Release,
Low Warpage,
Wear Resistant

Applications & Uses

Markets: Electrical & Electronics,
Industrial
Applications: Industrial — Chemical & Industrial Manufacturing
Equipment & Parts
Electrical & Electronics — Devices & Assemblies
Industrial Automation
Electrical & Electronics — Parts & Components
Semiconductor Manufacturing
Industrial — Power, Water & Utilities
Renewable Energy
Plastics & Elastomers End Uses: Electrical/Electronic Applications,
Energy Management,
Industrial Applications,
Semiconductor Applications
Plastics & Elastomers Processing Methods: Injection Molding

Properties

Flame Rating: UL 94 V0
Mechanical Properties
Physical Properties
Thermal Properties
Impact Properties
Injection Molding
Flame Characteristics
Note: ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.

¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

	Value	Units	Test Method / Conditions
Tensile Stress (Yield, Type I, 5 mm/min) ¹¹	14	MPa	ASTM D638
Tensile Stress (Break, Type I, 5 mm/min) ¹¹	12	MPa	ASTM D638
Tensile Strain (Yield, Type I, 5 mm/min) ¹¹	5.5	%	ASTM D638
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	9.3	%	ASTM D638
Tensile Modulus (at 50 mm/min) ¹¹	1010	MPa	ASTM D638
Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹	20	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	790	MPa	ASTM D790
Tensile Stress (Yield, 5 mm/min) ¹¹	14	MPa	ISO 527
Tensile Stress (Break, 5 mm/min) ¹¹	13	MPa	ISO 527
Tensile Strain (Yield, 5 mm/min) ¹¹	6.1	%	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	9.3	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	930	MPa	ISO 527
Flexural Stress ¹¹	19	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	870	MPa	ISO 178

	Value	Units	Test Method / Conditions
Specific Gravity ¹¹	2.17	-	ASTM D792
Density ¹¹	2.17	g/cm³	ASTM D792
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹	0.01	%	ASTM D570

	Value	Units	Test Method / Conditions
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹	79	°C	ASTM D648
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	57	°C	ASTM D648
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80104, sp=64mm) ¹¹	80	°C	ISO 75/Bf
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80104, sp=64mm) ¹¹	61	°C	ISO 75/Af

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	120 - 150	°C	-
Drying Time ⁷	4	Hrs	-
Melt Temperature ⁷	370 - 390	°C	-
Front - Zone 3 Temperature ⁷	380 - 400	°C	-
Middle - Zone 2 Temperature ⁷	380 - 400	°C	-
Rear - Zone 1 Temperature ⁷	360 - 380	°C	-
Mold Temperature ⁷	200 - 220	°C	-
Back Pressure (Plastic Pressure) ⁷	2.5 - 2.9	MPa	-

	Value	Units	Test Method / Conditions
UL Compliant (94V-0 Flame Class Rating)	1.5	mm	UL 94 by SABIC-IP

Regulatory & Compliance

Packaging & Availability

LNP™ LUBRICOMP™ Compound 2X00858