Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Composite Materials Functions
- Technologies
Features & Benefits
Applications & Uses
- Applications
- Composites End Use
- Composites Processing Methods
- Plastics & Elastomers Processing Methods
Properties
- Color
- Flame Rating
- Processing Information (Injection Molding)
- Processing Information (Compression Molding)
- Processing Information (Transfer Molding)
Value | Units | Test Method / Conditions | |
Apparent Density | 0.65 | g/cm³ | ASTM D1895 |
Arc Resistance | 141 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 6.3e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 166 | V | ASTM D3638 |
Compressive Strength | 199 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 159 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 9.4 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.076 | - | ASTM D150 |
Flexural Modulus | 7481 | MPa | ASTM D790 |
Flexural Strength | 86.7 | MPa | ASTM D790 |
Heat Resistance | 201 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 99 | J/m | Plenco |
Impact Strength (Notched, Izod) | 17.1 | J/m | ASTM D256 |
Impact Strength (Notched, Charpy) | 17.8 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0098 | m/m | ASTM D6289 |
Oxygen Index | 26.5 | % | ASTM D2863 |
Permittivity (at 1MHz) | 5.2 | - | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.43 | % | ASTM D6289 |
Rockwell Hardness | 83 | E-Scale | ASTM D785 |
Specific Gravity | 1.41 | - | ASTM D792 |
Tensile Elongation | 0.8 | % | ASTM D638 |
Tensile Modulus | 8452 | MPa | ASTM D638 |
Tensile Strength | 59 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.41 | W/m/°C | ASTM E1461 |
UL Flammability (at 1.5mm) | HB | - | UL 94 |
Volume Resistivity | 1600000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.42 | % | ASTM D570 |
Value | Units | Test Method / Conditions | |
Apparent Density | 0.59 | g/cm³ | ASTM D1895 |
Arc Resistance | 134 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 6.3e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 160 | V | ASTM D3638 |
Compressive Strength | 208 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 176 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 14 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.046 | - | ASTM D150 |
Flexural Modulus | 8592 | MPa | ASTM D790 |
Flexural Strength | 92.8 | MPa | ASTM D790 |
Heat Resistance | 196 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 136 | J/m | Plenco |
Impact Strength (Notched, Charpy) | 19.9 | J/m | ASTM D256 |
Impact Strength (Notched, Izod) | 20.7 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0034 | m/m | ASTM D6289 |
Oxygen Index | 26.5 | % | ASTM D2863 |
Permittivity (at 1MHz) | 5.1 | - | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.23 | % | ASTM D6289 |
Rockwell Hardness | 88 | E-Scale | ASTM D785 |
Specific Gravity | 1.41 | - | ASTM D792 |
Tensile Elongation | 0.7 | % | ASTM D638 |
Tensile Modulus | 9304 | MPa | ASTM D638 |
Tensile Strength | 55 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.41 | W/m/°C | ASTM E1461 |
UL Flammability (at 1.5mm) | HB | - | UL 94 |
Volume Resistivity | 2200000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.53 | % | ASTM D570 |
Value | Units | Test Method / Conditions | |
Apparent Density | 0.62 | g/cm³ | ASTM D1895 |
Arc Resistance | 141 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 6.3e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 161 | V | ASTM D3638 |
Compressive Strength | 203 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 168 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 10 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.06 | - | ASTM D150 |
Flexural Modulus | 7579 | MPa | ASTM D790 |
Flexural Strength | 73.5 | MPa | ASTM D790 |
Heat Resistance | 200 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 99 | J/m | Plenco |
Impact Strength (Notched, Izod) | 17.5 | J/m | ASTM D256 |
Impact Strength (Notched, Charpy) | 19.6 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0074 | m/m | ASTM D6289 |
Oxygen Index | 26.5 | % | ASTM D2863 |
Permittivity (at 1MHz) | 5.5 | - | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.31 | % | ASTM D6289 |
Rockwell Hardness | 85 | E-Scale | ASTM D785 |
Specific Gravity | 1.42 | - | ASTM D792 |
Tensile Elongation | 0.7 | % | ASTM D638 |
Tensile Modulus | 8341 | MPa | ASTM D638 |
Tensile Strength | 51 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.41 | W/m/°C | ASTM E1461 |
UL Flammability (at 1.5mm) | HB | - | UL 94 |
Volume Resistivity | 640000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.35 | % | ASTM D570 |
Regulatory & Compliance
- Certifications & Compliance