Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Product Type
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Ready-to-Use Product Features
- Key Attributes
- Creates durable, reliable and conductive traces
- Typical trace width: 1.5–2.0 mm
- Dries in 1 minute at room temperature
- Strong corrosion resistance
- Does not contain toluene, xylene, or MEK
Applications & Uses
- Markets
- Applications
- Application Area
- Cure Instructions
- Allow to dry at room temperature for 24 hours, or after letting sit for 1 minute, cure the coating in an oven for 30 minutes @ 65 ˚C.
- Recommended Preparation
- Clean the substrate with Isopropyl Alcohol, MG #824, so the surface is free of oils, dust, and other residues.
- Application Instructions
- Shake pen vigorously until the ball moves freely inside.
- Hold pen at angle and depress tip against surface.
- Draw pen across surface while gently squeezing barrel.
- Let dry 1 min before handling or heat cure.
- Clean tip, replace cap and store tip up after use.
Properties
- Physical Form
- Physical Properties
- Typical Properties
- Cured Properties
- Uncured Properties
Value | Units | Test Method / Conditions | |
Density | 1.51 | g/mL | - |
Value | Units | Test Method / Conditions | |
Approximate Linear Coverage | 30 | Minutes | - |
Calculated VOC | 337 | g/L | - |
Cure Times (at 22 ˚C) | 24 | Hours | - |
Cure Times (at 65 ˚C) | 30 | Minutes | - |
Dry to Touch | 1 | Minutes | - |
Viscosity (at 25 ˚C) | 160 | cP | - |
Value | Units | Test Method / Conditions | |
Resistivity | 4 x 10⁻³ | Ω·cm | - |
Service Temperature Range | -40 to 120 | ˚C | - |
Value | Units | Test Method / Conditions | |
Solids Content | 57 | % | - |
Regulatory & Compliance
- Certifications & Compliance
- Chemical Inventories
Packaging & Availability
- Available Packaging
Cat. No. Packaging Net Vol. Net Wt. 841AR-P Pen 5 mL 7.57 g
Storage & Handling
- Shelf Life
- 3 Years
- Storage and Handling
- Store between -5 and 22 ˚C in a dry area, away from sunlight (see SDS).