Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Reinforcement Material
- Composite Materials Functions
- Technologies
Features & Benefits
Applications & Uses
- Applications
- Composites End Use
- Composites Processing Methods
- Plastics & Elastomers Processing Methods
Properties
- Color
- Flame Rating
- Physical Form
- Processing Information (Injection Molding)
- Processing Information (Transfer Molding)
Value | Units | Test Method / Conditions | |
Apparent Density | 0.7 | g/cm³ | ASTM D1895 |
Arc Resistance | 180 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 4.6e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 188 | V | ASTM D3638 |
Compressive Strength | 150 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 196 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 11.5 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.056 | - | ASTM D150 |
Flexural Modulus | 9581 | MPa | ASTM D790 |
Flexural Strength | 88.2 | MPa | ASTM D790 |
Heat Resistance | 190 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 169 | J/m | Plenco |
Impact Strength (Notched, Charpy) | 20.7 | J/m | ASTM D256 |
Impact Strength (Notched, Izod) | 23.6 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0061 | m/m | ASTM D6289 |
Oxygen Index | 34.8 | % | ASTM D2863 |
Permittivity (at 1MHz) | 4.9 | - | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.23 | % | ASTM D6289 |
Rockwell Hardness | 68 | E-Scale | ASTM D785 |
Specific Gravity | 1.55 | - | ASTM D792 |
Tensile Elongation | 0.8 | % | ASTM D638 |
Tensile Modulus | 9241 | MPa | ASTM D638 |
Tensile Strength | 51 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.57 | W/m/°C | ASTM E1461 |
UL Flammability (at 6mm) | V-0 | - | UL 94 |
Volume Resistivity | 260000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.21 | % | ASTM D570 |
Value | Units | Test Method / Conditions | |
Apparent Density | 0.68 | g/cm³ | ASTM D1895 |
Arc Resistance | 184 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 4.6e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 177 | V | ASTM D3638 |
Compressive Strength | 157 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 192 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 11.8 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.055 | - | ASTM D150 |
Flexural Modulus | 9371 | MPa | ASTM D790 |
Flexural Strength | 86 | MPa | ASTM D790 |
Heat Resistance | 196 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 138 | J/m | Plenco |
Impact Strength (Notched, Izod) | 24.1 | J/m | ASTM D256 |
Impact Strength (Notched, Charpy) | 24.6 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0041 | m/m | ASTM D6289 |
Oxygen Index | 34.8 | % | ASTM D2863 |
Permittivity (at 1MHz) | 5.4 | - | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.19 | % | ASTM D6289 |
Rockwell Hardness | 73 | E-Scale | ASTM D785 |
Specific Gravity | 1.56 | - | ASTM D792 |
Tensile Elongation | 0.7 | % | ASTM D638 |
Tensile Modulus | 9145 | MPa | ASTM D638 |
Tensile Strength | 48 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.57 | W/m/°C | ASTM E1461 |
UL Flammability (at 6mm) | V-0 | - | UL 94 |
Volume Resistivity | 600000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.15 | % | ASTM D570 |