SLL5405S

Identification & Functionality

Additives Included

Anti-Blocking Agent,

Slip Agent

Chemical Family

Polyethylenes,

Polyolefins

Polymer Name

Linear Low Density Polyethylene (LLDPE)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Basic Thermoplastics

Polyolefins

Features & Benefits

Labeling Claims

Bio-based,

Low Carbon Footprint (PCF),

Sustainable,

Sustainable Polyethylene

Materials Features

Excellent Performance,

Excellent Sealability,

Good Mechanical Properties,

Good Processability,

Low Carbon Content,

Low Gel

Applications & Uses

Plastics & Elastomers End Uses

Film

Plastics & Elastomers Processing Methods

Blown Film Extrusion,

Extrusion,

Film Extrusion

Properties

Blown Film Properties

	Value	Units	Test Method / Conditions
Tensile Strength (at Break, MD)	40.0	MPa	ASTM D882
Tensile Strength (at Break, TD)	30.0	MPa	ASTM D882
Elongation (at Break, MD)	1070.0	%	ASTM D882
Elongation (at Break, TD)	1340.0	%	ASTM D882
Tensile Modulus (1% Secant, MD)	210.0	MPa	ASTM D882
Tensile Modulus (1% Secant, TD)	230.0	MPa	ASTM D882
Dart Drop Impact Strength	130.0	g/F50	ASTM D1709
Elmendorf Tear Strength (MD)	180.0	gF	ASTM D1922
Elmendorf Tear Strength (TD)	400.0	gF	ASTM D1922

Control Properties

	Value	Units	Test Method / Conditions
Melt Flow Rate (at 190°C, 2.16kg)	1.0	g/10 min	ASTM D1238
Density	0.918	g/cm³	ASTM D 792

Note

Blown Film Properties:

• Film with 38 microns produce in a 40mm extruder and a blow‐up ratio of 2.2:1. (MD = extrusion direction and TD = transversal direction).